Retroreflective sheet coated with silica layer

ABSTRACT

Retroreflective sheeting has been improved by a coating comprising silica and a transparent polymer selected from aliphatic polyurethanes and polyvinyl chloride copolymers having a minor amount of a comonomer containing at least one carboxylic acid or hydroxyl moiety. Silica comprises 10-80 weight percent of the transparent protective coating. For example, a solution or dispersion of polyurethane is mixed with a silica sol and possibly other ingredients (e.g. wetting agent, UV light absorber and adhesion promoter), and the composition is coated onto the retroreflective sheet and dried. The coated retroreflective sheeting has superior soil and dew repellancy, retaining a higher percentage of original brightness after exposure to dirt and/or dew conditions.

TECHNICAL FIELD

This invention is in the field of retroreflective sheeting and specialized coatings for such sheeting to impart soil repellency and other beneficial properties. Specifically, the invention relates to coatings containing silica and to processes for preparing the coated compositions and for applying them to retroreflective sheeting.

BACKGROUND

There are several types of retroreflective sheeting: exposed lens (as taught in U.S. Pat. Nos. 2,326,634 and 2,354,018,embedded lens (see U.S. Pat. No. 2,407,680; 4,367,920 and 4,505,967) and encapsulated lens (see U.S. Pat. No. 4,025,159). The drawings of the aforementioned patents illustrate the various sheeting types and are incorporated by reference herein. Retroreflective sheeting, in general, comprises a multiplicity of lens elements and a reflector located behind the lens elements. The lens elements may be, for example, glass or ceramic microspheres in a polymeric base sheet. The reflector may be: a layer of reflective metal (e.g. aluminum which has been vapor deposited on the lens elements or at some location behind the lens elements); flakes of reflective metal embedded in a binder layer; or a dielectric reflector as taught in U.S. Pat. No. 3,700,305.

Exposed lens retroreflective sheeting generally comprises a polymeric binder film in which is partially embedded a multiplicity of lens elements (e.g. glass microspheres), and a reflecting means disposed on the back (embedded) side of the lens elements.

Embedded or enclosed lens sheeting may be comprised of: a back reflector; an overlying transparent spacing layer; a layer of small lens elements embedded in the spacing layer and in optical connection with the reflector and spaced from it so as to place the reflector at the approximate focal point of the lens elements; a transparent covering layer conforming to the front extremities of the lens elements and having a flat front face; and an optional transparent top layer for improving weatherability.

Encapsulated lens retroreflective sheeting may, for example, be comprised of a plurality of glass microspheres having their back surfaces partially embedded in a transparent polymeric layer with a reflective layer adjacent to and disposed behind the embedded back surfaces of the microspheres and another transparent polymeric layer over the front of the microspheres and bonded to the first transparent polymeric layer in such a way as to result in air cells in front of the microspheres.

Retroreflective sheeting has many applications. Exposed lens sheeting with a dielectric reflector is used as a security film placed on top of documents such as driver's licenses, passports, and automobile titles. They can bear identifying indicia such as a state seal or watermark which can be seen at certain angles, but which do not interfere with the legibility of the document. Exposed lens sheeting is also useful as a safety item on garments to make them reflective at night, such as policeman's uniforms, fireman's coats and jogging outfits. Both enclosed and encapsulated lens sheeting are useful in applications where they will be exposed to rain because the clear plastic layer which lies over the microspheres or other lens elements helps to prevent water droplets from adversely affecting the optics of the lenses. Thus, embedded lens sheeting is used in license plates and validation stickers for automobiles, and both encapsulated lens and enclosed lens sheeting have been used in highway signs and reflectors.

In use on highway signs and reflectors (e.g. pavement delineators placed on the road) it is desirable for sheeting to be soil resistant and dew repellent. The accumulation of dirt and oil from the air and road surface onto retroreflective sheeting is detrimental to the retention of its retroreflective brightness. Thus, the term "soil repellent" means being nonadherent to dirt particles.

It is well known that droplets of water (e.g., dew) can condense from a humid atmosphere onto a cool surface. Such condensation formed upon the surface of retroreflective sheeting impairs the transmission of light through it. The term "dew modifier" as applied to retroreflective sheeting means a material which is able to avoid a substantial decrease of retroreflective brightness due to formation of water droplets on the surface, for example by causing the dew or water to wet the surface and form a sheet or layer of water rather than droplets.

It is also desirable for the sheeting to be abrasion resistant, especially when it is to be used on the road surface. Retroreflective sheeting is applied to road surfaces in the form of pavement marking tape and as the reflective element in pavement delineators or pavement markers. In these applications, the sheeting is actually contacted by vehicle tires as they traverse the pavement markers or lane marking tape. The force of the tires, combined with any road grit, can abrade the reflective sheeting.

The use of silica coatings to modify the surface of light transmissive materials is known (e.g. antireflective coatings). However, the desired combination of soil repellency and dew modification have not yet been obtained with a silica coating that is able to tenaciously adhere to retroreflective sheeting.

DISCLOSURE OF INVENTION

Retroreflective sheeting has now been improved by applying a polymer coating containing silica. The invention is summarized as a soil resistant and dew repellent reflective sheet having a transparent protective coating comprising a mixture of silica and

a transparent polymer selected from the group consisting of:

aliphatic polyurethanes, and

polyvinylchloride copolymers having a minor portion (i.e. less than 10 weight percent) of a comonomer containing at least one carboxylic acid or hydroxyl moiety,

wherein the silica comprises about 10-80 wt.% of the transparent protective coating.

As used above, the term transparent means transmitting at least 90% of incident light in the visible spectrum (about 400-700 nm wavelength). This has been determined using an IBM model 9420 UV-visible spectrophotometer. The inventive protective coating was applied to polyester film about 55 micrometers thick. The dry protective coatings on the samples used had a thickness of about 2.5 to 7.6 micrometers. The light transmittance through the uncoated polyester and through coated samples was measured at various wavelengths. In all cases there was only a slight difference in light transmittance between the coated and uncoated polyester (≦3% ±) regardless of percent silica in the protective coating or wavelength, indicating that transmittance through the protective coating was greater than 97%.

The term aliphatic polyurethane means a polyurethane derived from at least one aliphatic polyisocyanate preferably without any aromatic polyisocyanate. Aliphatic polyisocyanates known to the art are: 1,4-cyclohexane bis(methyleneisocyanate); methylcyclohexylene diisocyanate; 1,4-cyclohexanyl diisocyanate; dicyclohexylmethane diisocyanate; 1,6-diisocyanato-2,2,4,4-tetramethylhexane; 1,6-diisocyanato-2,4,4-trimethylhexane; ##STR1## wherein R₃ is --CH₃ or --C₂ H₅ ; and isophorone diisocyanate. The polyols used for aliphatic polyurethanes may be polyester or polyether polyols.

The inventive protective coating can be made permanent. For purposes of this description, the term "permanent" means a coating which is not rubbed off easily by hand and which is not readily removed by applying common pressure-sensitive adhesive tape and lifting the tape off of the coating.

The protective coating is the last coating applied to the retroreflective sheet. The retroreflective sheet itself may comprise several layers, as described previously, and the term "top layer" will be used herein to refer to top-most layer of the retroreflective sheet just before the protective coating is applied. Thus, as to the retroreflective sheet, the light must pass first through the protective coating and next through the top layer in order to pass through the lens elements and reach the reflector. Typical top layers for retroreflective sheets are comprised of polyacrylate (e.g., polymethylmethacrylate), polyurethane (typically aliphatic polyurethane), polyvinyl (e.g., polyvinyl-chloride) or polycarbonate polymers. The protective coating of this invention has been found to adhere very well to such top films without affecting the retroreflective brightness of the sheet. The modified sheeting has good soil repellency and anti-fogging properties (i.e., dew modification) and are suitable for use in pavement markings, roadway delineators, vehicle license plates and signing products.

The mixtures which are used as coating compositions for the protective coating can be formulated by mixing various concentrations of silica sol (aquasol, hydrosol or colloidal dispersion) with aliphatic polyurethane or polyvinyl chloride copolymers in organic solvents or water dispersion. Silica sol colloid particle size is an important factor for preparing a clear and transparent protective coating. The colloid particles should be less than about 50 nanometers (nm) in diameter, preferably no greater than 20 nm in diameter. In the dry protective coatings, the silica particles agglomerate, but individual particles are discernible and have been measured in the range of 0-40 nm diameter or particle size, 15-34 nm to be precise.

BRIEF DESCRIPTION OF THE DRAWING

The FIGURE is a graph of brightness retention versus time in minutes for various retroreflective sheet materials exposed to dew conditions. All of the retroreflective sheeting materials tested were of the enclosed lens type and had a vinyl top layer. All samples were exposed to the same conditions in which water droplets condensed on the sheeting surface, and the graph represents the initial loss in retroreflective brightness and the recovery of brightness over time. The solid line is for the control, Scotchlite 680 reflective sheeting, and lines Nos. 1, 2 and 3 represent various embodiments of the invention coated with a mixture comprising 30% silica, with the remainder being comprised of a polymer and (in the case of lines 2 and 3) a wetting agent.

DETAILED DESCRIPTION

The raw materials selected for making the inventive protective coating should not adversely affect the retroreflective sheeting to which they are applied. For example, they should not require drying conditions which would distort the sheeting and the relationship between the lens elements and the reflector. They should also not contain solvents or other ingredients which would dissolve or corrode the sheeting components. Coating mixtures containing toluene, isopropanol and/or butyl cellosolve have been found suitable for use with retroreflective sheeting.

Colloidal silica dispersions are available commercially with different colloid sizes. Two such dispersions which have been found useful are: Nyacol 1440 colloidal silica, having a colloid size of 14 nm, a Na₂ O content of 0.48 weight percent and a concentration of 40 weight percent silica, available from Nyacol Products, Inc., of Ashland, Md.; and Nalco 1140 silica, having a mean particle size of 15 nm, a Na₂ O concentration of 0.40 weight percent and a concentration of 40 weight percent silica in water, available from Nalco Chemical Company of Oakbrook, Ill. Both are suspended in alkaline aqueous media. Other colloidal silica dispersed in glycol ether solvent; e.g., Nalco 84SS-258 silica from Nalco Chemical Co. having a silica particle size of about 20 nm, can be used with polymer resins dissolved in organic solvent.

It is preferred that the polymer mixed with the silica sol is at least somewhat elastic, especially in cases where the retroreflective sheeting is to be applied to a flexible substrate, such as a rubber pavement marker. Several of the polymers which have been found useful are given below, (all monomer percents expressed being weight percent):

Aliphatic Polyurethanes:NeoRez R-960 Polyurethane, a flexible polyurethane sold in 33% by weight concentration in water by Beatrice Chemical Company, Division of Beatrice Foods Company, Wilmington, Mass. This polyurethane is believed to be derived from the following monomers: ##STR2## Its molecular weight is believed to be at least 200,000. When the NeoRez polyurethane is used, it has also been found useful to include an aziridine crosslinking compound to improve the physical properties of the final coating. The cross-linking compound used in the development of this invention has been CX-100 cross-linker from Beatrice.

Permuthane U-6729 urethane resin sold in a 1:1 mixture of isopropanol and toluene at a concentration of 25% resin by Beatrice Chemical Division of Beatrice Foods. This resin is believed to be derived from the following monomers: dicyclohexylmethane diisocyanate; adipic acid; neopentyl glycol; and 1,6-hexanediol. It is believed to have a weight average molecular weight (Mw) of about 33,000 and a number average molecular weight (Mn) of about 11,000.

Permuthane U-23-327 urethane resin sold in a 1:1 mixture of isopropanol and toluene or methyl cellosolve at a concentration of about 35% resin by Beatrice.

Although the polyurethanes used in making this invention have not been the radiation curable variety, e.g. with acrylate or methacrylate end groups, such polyurethanes may be used.

The molecular weight of the polyurethane is preferably over 20,000.

Polyvinyl chloride copolymers:

VROH copolymer, believed to have the following monomer content: vinyl chloride (79-83%), vinyl acetate (5%), and vinyl alcohol (≦15%). It is said to have 1.8-2.2% by weight hydroxyl content.

VMCH Copolymer believed to have the following monomer content: vinyl chloride (85-88%), maleic acid (0.8-1.2%) and vinyl acetate (about 13%). Besides maleic acid, acrylic and methacrylic acids may be incorporated into the useful polyvinyl chloride copolymers.

VAGH partially hydrolyzed copolymer believed to have the following monomer content: vinyl chloride (89.5-91.5%), vinyl acetate (3%) and vinyl alcohol (5.2-6.5%). VROH, VMCH and VAGH copolymers are available from Union Carbide Corporation.

Other compounds which have been found useful for incorporation into the coating composition of this invention are:

Polyalkylene oxide modified dimethylpolysiloxanes which are polymeric wetting agents sold under the trademark Silwet® by Union Carbide Corporation. The general formula for Silwet copolymers stated in Union Carbide literature is: ##STR3##

Ultraviolet light stabilizers or absorbers, to improve the stability and weatherability of the protective coating. One suitable ultraviolet light absorber is Tinuvin 328 general purpose UV absorber by Ciba-Geigy Corporation of Ardsley, N.Y. Ciba-Geigy literature indicates that Tinuvin 328 light absorber has the following formula: ##STR4## wherein

R₁ and R₂ are t-amyl.

A retroreflective sheeting used in reducing the invention to practice was a wide angle flat top sheet which comprises, in general: a back reflector of vapor deposited aluminum; and overlying transparent matrix; a light-returning layer of transparent microspheres embedded in the transparent matrix and in optical connection with the reflector but spaced from it so as to place the reflector at the approximate focal point of the microspheres; and a transparent overlying solid covering which conforms to the front extremities of the microspheres and has a flat front face. Such sheeting reflects a cone of light back toward a light source even though the incident light beam strikes the sheeting at an angle.

Wide angle flat top retroreflective sheeting may be made, for example, by a solution casting technique comprising the following process steps: (a) providing a paper carrier web coated with a release agent such as polyethylene; (b) coating the release agent side of the carrier web with a 25% solids solution of fully reacted aliphatic elastomeric polyurethane of the polyester type in an isopropanol, toluene, xylene solvent in sufficient amount to yield about a 50 micrometers dry film thickness; (c) drying the coating from step (b) for example at about 90° C. for 15 minutes; (d) applying a bead bond coat about 5 micrometers thick of the same polyurethane material used in step (b) to the dry coating from step (c) and contacting the wet polyurethane surface with glass microspheres (e.g., about 20-120 micrometers diameter and 1.9-2.5 refractive index); (e) drying the microsphere-coated web for example at 93° C. for 5 minutes; (f) coating a spacing layer polymer of the same aliphatic elastomeric polyurethane composition onto the microsphere-covered web or sheet from step (e) in sufficient amount to yield a dry film thickness about equal to the focal length of the microspheres; (g) drying the sheeting from step (f); (h) vapor coating the spacing layer with a specularly reflective material (e.g., aluminum); (i) removing the paper carrier web; and (j) coating the back side of the reflective material with an acrylate-base pressure-sensitive adhesive having a silicone coated release liner.

The soil resistant reflective sheeting of this invention is prepared by the following steps:

A. The protective coating composition is prepared by mixing colloidal silica with one of the selected polymers, such as polyurethane, and any other desired ingredients, such as light stabilizer or cross-linking agent;

B. A retroreflective sheet is provided, and it is coated with the protective coating composition by conventional means, such as a wire wound bar, knife coating or dip coating; and

C. The wet coating from step B is dried and cured by placing the retroreflective sheet in an oven.

The details of each of the above steps will now be explained. In one preferred sequence for step A, the protective coating composition is prepared as follows:

(1) Dilute Permuthane U-6729 polyurethane solution with a 1:1 volume ratio mixture of toluene and isopropanol to about 25% concentration.

(2) Dissolve Tinuvin 328 light stabilizer in the same solvent mixture as in step (1) above, and add to the solution from step (1).

(3) To the solution from step (2), slowly add colloidal silica (30% solids) and mix.

(4) To the mixture from step (3), add hydrophilic Silwet L-77 siloxane wetting agent and mix.

(5) Mix in minor amount (<10 weight percent) of Silane X1-6106 adhesion promoter from Dow Corning Corporation and mix gently to obtain a homogeneous colloidal silica suspension.

It is desirable not to add the colloidal silica as the last part of step A, because small gel particles can be formed, and the coating may become hazy. The concentration of SiO₂ in the final dry coating is between about 15 and 60 weight percent.

When using the polyvinyl chloride transparent polymers, they are normally furnished dissolved in organic solvent (e.g. 10 weight percent in methyl ethyl ketone). In that case, silica is also furnished in an organic medium, e.g. Nalco 84SS-258 colloidal SiO₂ dispersion in glycol ether.

The protective coating has good adhesion to retroreflective sheeting with a polyurethane top layer. However, for retroreflective sheeting with a polyacrylate top layer, it has been found desirable to pretreat the sheeting with corona treatment to improve adhesion between the sheeting and the protective coating. A general discussion of corona treatment of webs for improving adhesion is found in Cramm, R. H. and Bibee, D. V., "The Theory and Practice of Corona Treatment for Improving Adhesion", TAPPI, August, 1982, pp. 75-78. The apparatus used in such corona treatment has been a Softal Electric Company machine from West Germany, Model 3025DW, having 1.2 Kw maximum power and electrode 0.56 m long. Sheeting has been treated using a current of 180-300 milliamps and drawing the sheeting through the apparatus at a rate of 10-100 m/min. for a sheet about 0.3m wide. One typical treatment level is about 14 Watts/ft²,/min. (150 w/m² /min).

The concentration ranges for the minor ingredients in the protective coating composition are: for the hydrophilic siloxane, 0-5 weight percent, preferably about 3%; for the silane adhesion promoter 0-3%; and for the light stabilizer (Tinuvin 328) 0-6 weight percent, preferably 2-4%.

The conditions for step C are generally about 50°-93° C. for 1-5 minutes in an air atmosphere. Generally, retroreflective sheeting having a polyurethane top layer can withstand somewhat higher temperatures, and a curing condition of 93° C. for 2-3 minutes is appropriate. However, in the case of polyacrylate top layers, conditions are preferably about 65°-71° C. for 1-3 minutes. Thickness of the final protective coating is generally less than 150 micrometers.

The invention will be further clarified by the following examples, which are intended to be purely exemplary. In the examples, percentages of protective coating constituents are expressed as weight percent taking the total of SiO₂ and the transparent polymer (e.g., polyurethane or polyvinylchloride copolymer) as 100%.

EXAMPLE I

In the case of the vinyl resins used in this invention, the stability of the protective coating composition (as measured by retention of brightness) has been found somewhat dependent on SiO₂ concentration. This is shown by the following table:

                  TABLE 1                                                          ______________________________________                                                                        Brightness                                      Sample  Vinyl Resin  SiO.sub.2, Wt %                                                                          Retention                                       ______________________________________                                         A       VAGH         20        98                                              B       VAGH         30        95                                              C       VAGH         40        86                                              D       VAGH         50        26                                              E       VMCH2        20        102                                             F       VMCH2        30        102                                             G       VMCH2        40        100                                             H       VMCH2        50        96                                              ______________________________________                                    

The above data show that the SiO₂ is quite stable in the VMCH2 vinyl resin from Union Carbide Corporation; whereas, above 30 weight percent concentration, it becomes less stable in the VAGH resin. A white precipitate was formed in some of the VAGH resin mixtures. Therefore, within the class of vinyl copolymers described, some experimentation is required to discern those which are useful and the concentration limits within which they are useful.

EXAMPLE II

In soil repellency tests, retroreflective sheeting samples were mechanically splashed with road dirt and water containing a trace amount of vehicle motor oil. The retroreflectivity retention of splashed and dried specimens was tested using a retroluminometer after each test cycle. The brightness retention corresponding to each test cycle is shown in Table 2 below:

                  TABLE 2                                                          ______________________________________                                         Sample    Control    23-A   27-A   27-B 27-F                                   ______________________________________                                         Wt % SiO.sub.2                                                                            0         33     33     25   60                                     Silwet    no         no     yes    yes  yes                                    Siloxane                                                                       Organic   --         --     x      x    x                                      base                                                                           H.sub.2 O base                                                                           --         x      --     --   --                                     % Initial                                                                      Brightness                                                                     Retained                                                                       after:                                                                         1st cycle 58         75     92     91   91                                     2nd cycle 42         68     88     86   87                                     3rd cycle 44         75     85     86   85                                     4th cycle 46         76     83     82   81                                     ______________________________________                                    

In the above table, the control was an encapsulated lens retroreflective sheeting which is used in traffic signs, and all of the other samples were specimens of the same type of sheeting modified in accordance with this invention. In each of the inventive samples, the transparent polymer used was a polyurethane, and the term organic base means that the polyurethane was dissolved in organic solvent, while the term H₂ O base means that the polyurethane was dispersed in water. The data show that the inventive retroreflective sheeting samples retained more than 80% of their initial brightness, while the uncoated control retained only about 46%. The data also indicate that the presence of a small amount of the hydrophilic siloxane wetting agent may enhance the soil repellency without adversely affecting brightness.

EXAMPLE III

Dew tests were performed in accordance with the following procedure. Samples of retroreflective sheeting were laminated to aluminum panels which were placed in direct contact with the outside surface of a rectangular, galvanized metal box filled with ice water. As the samples cooled, moisture in the air gradually condensed on their surfaces to form water droplets. A portable retroreflectometer was used to monitor the brightness of the sheeting samples over time. The retroreflectometer used was made by Retro-Tech of La Mesa, Calif. and it reads in units of candela per lux-meters squared (cd/lux-m²). The results are indicated on the FIGURE attached. The solid line is the plot for the control sample, Scotchlite 680 retroreflective sheeting. The other three plots are for specimens which were the same as the control, except that they had been coated with the inventive protective coating. In all three of those cases, the concentration of SiO₂ was about 30%. For line no. 1, the protective coating contained no siloxane wetting agent. For line 2, the protective coating contained 3 weight percent Silwet siloxane wetting agent, and for the specimen represented in line 3, the protective coating contained 5 weight percent Silwet wetting agent.

From the figure, one can see that the initial loss of brightness over approximately the first five minutes was about the same for all four of the test specimens, but the recovery of brightness was quite different. It is evident that the wetting agent helps in the rapid recovery of brightness, since specimen 3 recovered about 87% of its brightness in 30 minutes. In other similar tests in which all conditions were kept constant except for silica concentration, it was found that specimens with higher silica content appeared to retain more of their brightness and recover a greater percentage of original brightness over time.

Thus, the protective coating has been made hydrophilic. That is, it is readily wetted by water. Hydrophilic nature can be measured by the change in contact angle of a drop of water on the surface, over time, i.e. the angle between the side of the drop and the surface at the perimeter of the drop. For example, a contact angle which increases over time or remains high (e.g. over 70°) would exemplify a hydrophobic surface, whereas, a contact angle which decreases over time or remains low would exemplify a hydrophilic material. That is, on hydrophilic surfaces, water drops tend to spread out, while, on hydrophobic surfaces, water tends to form beads.

Although the protective coating can be made hydrophilic, it resists absorption of water deep into the coating where it could cause opacity. Even in dew conditions, the inventive retroreflective sheet remains clear and transparent.

EXAMPLE IV

Various embodiments of the retroreflective sheeting were made using the coating compositions as shown in Table 3 below. In each case, the coating composition was prepared by first mixing the polyurethane solution and silica sol together, adding the light absorber, then adding the siloxane wetting agent (if used). Finally, the silane adhesion promoter (if used) was added. In each case the coating composition was applied to the same type of retroreflective sheeting which was used in Example II. All of the coating compositions were coated by means of a wire wound coating bar (wire 0.914 mm diameter). the coated samples were dried in a forced air oven at about 66° C. for about 3-4 minutes. Each sample was subjected to an adhesion test similar to ASTM Test No. D-3359, using Scotch® 610 adhesive tape. The cross-hatch or lattice pattern was made in the coating samples and the adhesive tape was applied and removed in a similar manner to the ASTM Test, but results were reported as adhesion failure percent. That is, by visual observation, an estimate was made of how much of the protective coating was lifted off by the tape, indicating adhesive failure. The results reported are the average of more than three specimens. The adhesion test results and the compositions of the samples are reported in Table 3 below:

                                      TABLE 3                                      __________________________________________________________________________                           SiO.sub.2 sol         Silane*                            Polyurethane          (30% in glycol                                                                         Tinuvin                                                                               Siloxane                                                                              adhesion                           25% Solids     Toluene/                                                                              ether solvent)                                                                         light absorber                                                                        wetting agent                                                                         promoter                                   % of final                                                                            Isopropanol                                                                           % of final                                                                             % of final                                                                            % of final                                                                            % of final                                                                            Adhesion                    Sample                                                                             wt (g)                                                                             coating solids                                                                        1:1 wt (g)                                                                            coating solids                                                                         coating solids                                                                        coating solids                                                                        coating solids                                                                        failure                     __________________________________________________________________________                                                        %                           1   50  70     50     30      2                    0                           2   200 70     200    30      4                    0                           3   200 50     200    50      4                    0                           4   25  70     25     30      4      5             100                         5   25  70     25     30      4      3      2      10                          6   25  70     25     30      4      5      2      30                          7   25  70     25     30      4      8      2      100                         8   25  50     25     50      4      5             5                           9   25  50     25     50      4      3      2      0                           10  25  50     25     50      4      5      2      40                          11  25  50     25     50      4      8      2      100                         __________________________________________________________________________      *Added as 20% solution in isopropanol (75%) and H.sub.2 O (5%).                Weight reported is silane component only.                                

The above data show that, in general, increasing concentration of the siloxane wetting agent is detrimental to adhesion, while adding the silane adhesion promoter helps to overcome that effect. The adhesion of the inventive sheeting without either the wetting agent or the adhesion promoter appeared to be excellent.

In another test, the same type of retroreflective sheeting was treated with corona discharge and then coated with colloidal silica sol and dried at 66° C. or 93° C. for 3 minutes. The adhesion test showed poor adhesion of the resulting silica coating to the top layer of the reflective sheet, and the silica could be removed completely by wiping it with wet paper.

EXAMPLE V

Accelerated weathering tests have been conducted in QUV and KRC weatherometers. The results of the first 500 hours testing showed 90%-95% brightness retention for the inventive retroreflective sheet in which the protective coating contained 0.5%-1.5% Tinuvin 328 light stabilizer.

Other embodiments of this invention will be apparent to those skilled in the art from a consideration of this specification or practice of the invention disclosed herein. Various omissions, modifications and changes to the principles described herein, may be made by one skilled in the art without departing from the true scope and spirit of the invention which is indicated by the following claims. 

What is claimed is:
 1. A retroreflective sheet having a transparent, protective coating comprising silica and a transparent polymer selected from the group consisting of:aliphatic polyurethanes and polyvinyl chloride copolymers having a minor amount, not more than 15 weight percent, of comonomer containing at least one carboxylic acid or hydroxyl moiety,wherein the silica comprises about 10-80 weight percent of the transparent protective coating.
 2. The retroreflective sheet of claim 1 which further comprises a minor amount of hydrophilic polysiloxane polymer.
 3. The retroreflective sheet of claim 1 wherein the silica comprises particles less than 50 nm in particle size.
 4. The retroreflective sheet of claim 1 which is hydrophilic.
 5. The retroreflective sheet of claim 1 wherein the transparent polymer is a copolymer of vinyl chloride and at least one monomer selected from the group consisting of maleic acid, acrylic acid, methacrylic acid and vinyl alcohol.
 6. A retroreflective sheet having a transparent protective coating comprising silica and a transparent aliphatic polyurethane, wherein the silica comprises about 10-80 weight percent of the transparent protective coating.
 7. The retroreflective sheet of claim 6 wherein the aliphatic polyurethane contains an amount less than 10 weight percent of monomeric units having a carboxylic acid moiety.
 8. A process for making a retroreflective sheet having a protective silica coating comprising the steps of:A. preparing a protective coating composition by the steps of:(1) providing a transparent polymeric composition selected from the group consisting of aliphatic polyurethanes in water dispersion, aliphatic polyurethanes in organic solvent, and polyvinyl chloride copolymers having a minor amount, not more than 15 weight percent of a comonomer containing at least one carboxylic acid or hydroxyl moiety. (2) slowly mixing with the polymer from step (1) a silica sol, wherein the silica colloid particle size is less than 50 nm, in such a proportion to the polymeric composition from step (1) that the SiO₂ content is 10-80 weight percent of the total of SiO₂ plus the polymer solids from step (1); B. providing a retroreflective sheet and coating said retroreflective sheet with the protective coating composition from step A; and C. drying the coated retroreflective sheet from step B.
 9. The process of claim 8 which further comprises exposing the retroreflective sheet of step B to corona discharge before it is coated with the protective coating composition.
 10. The retroreflective sheet of claim 1 wherein the thickness of the protective coating is 2.5-150 micrometers. 